SS 410 Stainless Steel
Hardenable 12% chromium stainless with good strength and wear resistance. Magnetic.
Last updated:
What is SS 410?
SS 410 (UNS S41000, EN 1.4006) is a martensitic stainless steel containing 11.5–13.5% chromium and up to 0.75% nickel. Hardenable 12% chromium stainless with good strength and wear resistance. Magnetic. It has a density of 7.75 g/cm³ and a minimum tensile strength of 450 MPa, and is used mainly for pump and valve parts, cutlery and blades and fasteners.
- Type Martensitic (400 series)
- Equivalents UNS S41000 · EN 1.4006 · SUS 410
- Density 7.75 g/cm³
- Strength (min) 450 MPa tensile · 205 MPa yield
- Magnetic? Magnetic
- Main uses Pump and valve parts, cutlery and blades, fasteners
What is the chemical composition of SS 410?
Typical ASTM A240 limits, % by weight (single values are maximums).
| C | Mn | Si | P | S | Cr | Ni |
|---|---|---|---|---|---|---|
| 0.08 – 0.15 | 1.00 max | 1.00 max | 0.040 max | 0.030 max | 11.5 – 13.5 | 0.75 max |
What are the mechanical properties of SS 410?
| Tensile strength (min) | 450 MPa |
|---|---|
| Yield strength 0.2% (min) | 205 MPa |
| Elongation (min) | 20% |
| Hardness (max) | 96 HRB / 217 HB max (annealed) |
| Density | 7.75 g/cm³ |
What is the equivalent of SS 410?
| ASTM / AISI | UNS | EN / W.Nr. | DIN | JIS |
|---|---|---|---|---|
| 410 | S41000 | 1.4006 | X12Cr13 | SUS 410 |
Where is SS 410 used?
- Pump and valve parts
- Cutlery and blades
- Fasteners
- Turbine parts
- Petrochemical trays
Can SS 410 be welded?
Needs care: preheat to about 150–260 °C and temper after welding to avoid cracking, because it hardens in the weld zone.
Forming and machining
Machines well in the annealed condition and can then be hardened by heat treatment. It is magnetic.
SS 410 sizes we supply
Round bars, sheets, coils and strip — used for cutlery, valve parts and pump shafts.
SS 410 price compared with 304
Below 304, since it contains almost no nickel. For today's rate, send us your size and quantity.
Our advice
410 can be heat-treated to high strength but has lower corrosion resistance than 304. It is magnetic.
Values are typical ASTM A240 limits for flat products and are for guidance only. Always refer to the mill test certificate supplied with the material.
SS 410 — FAQs
What is the chemical composition of SS 410?
SS 410 contains 0.08–0.15% carbon, up to 1.00% manganese, up to 1.00% silicon, up to 0.040% phosphorus, up to 0.030% sulphur, 11.5–13.5% chromium and up to 0.75% nickel, with the balance iron (typical ASTM A240 limits).
What is the equivalent of SS 410?
SS 410 is UNS S41000, EN 1.4006 (X12Cr13) and SUS 410 in the Japanese standard.
What is the density of SS 410?
The density of SS 410 is about 7.75 g/cm³ (7750 kg/m³).
Where can I buy SS 410 in Vadodara?
Sagar Sales Corporation supplies SS 410 sheet, plate, coil, round bar, shims, slit coil in Vadodara with mill test certificates. Contact us for today's rate.
Get today's SS 410 rate
Tell us the grade, size, finish and quantity. We check stock and send a per-kg rate with dispatch date — usually the same working day.
- Rates direct from Vadodara stock
- Mill test certificate with every lot
- Cut-to-size and delivery all over India